ASTM A202 Steel vs. C64700 Bronze

ASTM A202 steel belongs to the iron alloys classification, while C64700 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is C64700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 17 to 18
9.0
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
44
Shear Strength, MPa 360 to 410
390
Tensile Strength: Ultimate (UTS), MPa 590 to 670
660
Tensile Strength: Yield (Proof), MPa 350 to 360
560

Thermal Properties

Latent Heat of Fusion, J/g 260
220
Maximum Temperature: Mechanical, °C 410
200
Melting Completion (Liquidus), °C 1450
1090
Melting Onset (Solidus), °C 1410
1030
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 52
210
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
38
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
38

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
31
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.4
2.7
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 49
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
57
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
1370
Stiffness to Weight: Axial, points 13
7.3
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 21 to 24
21
Strength to Weight: Bending, points 20 to 22
19
Thermal Diffusivity, mm2/s 14
59
Thermal Shock Resistance, points 17 to 20
24