ASTM A202 Steel vs. N08700 Stainless Steel

Both ASTM A202 steel and N08700 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is N08700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 200
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 18
32
Fatigue Strength, MPa 240
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 360 to 410
410
Tensile Strength: Ultimate (UTS), MPa 590 to 670
620
Tensile Strength: Yield (Proof), MPa 350 to 360
270

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
32
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.4
6.0
Embodied Energy, MJ/kg 19
82
Embodied Water, L/kg 49
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
160
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 24
21
Strength to Weight: Bending, points 20 to 22
20
Thermal Diffusivity, mm2/s 14
3.5
Thermal Shock Resistance, points 17 to 20
14