ASTM A202 Steel vs. S36200 Stainless Steel
Both ASTM A202 steel and S36200 stainless steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM A202 steel and the bottom bar is S36200 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 to 18 | |
| 3.4 to 4.6 |
| Fatigue Strength, MPa | 240 | |
| 450 to 570 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 360 to 410 | |
| 680 to 810 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 670 | |
| 1180 to 1410 |
| Tensile Strength: Yield (Proof), MPa | 350 to 360 | |
| 960 to 1240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 820 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 52 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 12 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 19 | |
| 40 |
| Embodied Water, L/kg | 49 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 93 to 96 | |
| 46 to 51 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 350 | |
| 2380 to 3930 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 42 to 50 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 32 to 36 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.3 |
| Thermal Shock Resistance, points | 17 to 20 | |
| 40 to 48 |