ASTM A203 Steel vs. EN 1.0033 Steel

Both ASTM A203 steel and EN 1.0033 steel are iron alloys.

For each property being compared, the top bar is ASTM A203 steel and the bottom bar is EN 1.0033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
86 to 96
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22 to 26
17 to 32
Fatigue Strength, MPa 210 to 280
120 to 140
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 330 to 370
200
Tensile Strength: Ultimate (UTS), MPa 520 to 590
300 to 330
Tensile Strength: Yield (Proof), MPa 290 to 390
150 to 200

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4 to 7.6
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5 to 8.7
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2 to 4.0
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.6 to 1.7
1.4
Embodied Energy, MJ/kg 21 to 23
18
Embodied Water, L/kg 50 to 52
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
48 to 83
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 410
63 to 100
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 21
10 to 12
Strength to Weight: Bending, points 18 to 20
13 to 14
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 15 to 17
9.4 to 10