MakeItFrom.com
Menu (ESC)

ASTM A203 Steel vs. N08904 Stainless Steel

Both ASTM A203 steel and N08904 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A203 steel and the bottom bar is N08904 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22 to 26
38
Fatigue Strength, MPa 210 to 280
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 330 to 370
370
Tensile Strength: Ultimate (UTS), MPa 520 to 590
540
Tensile Strength: Yield (Proof), MPa 290 to 390
240

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4 to 7.6
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5 to 8.7
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2 to 4.0
32
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 1.6 to 1.7
5.8
Embodied Energy, MJ/kg 21 to 23
79
Embodied Water, L/kg 50 to 52
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
170
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 410
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 21
19
Strength to Weight: Bending, points 18 to 20
18
Thermal Diffusivity, mm2/s 14
3.1
Thermal Shock Resistance, points 15 to 17
12