ASTM A209 Steel vs. EN 1.6982 Stainless Steel

Both ASTM A209 steel and EN 1.6982 stainless steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM A209 steel and the bottom bar is EN 1.6982 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 34
17
Fatigue Strength, MPa 180 to 200
350
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 420 to 460
800
Tensile Strength: Yield (Proof), MPa 220 to 250
570

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 410
770
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1420 to 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1 to 8.2
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
10
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.4
Embodied Energy, MJ/kg 20
33
Embodied Water, L/kg 47
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 170
820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15 to 16
28
Strength to Weight: Bending, points 16 to 17
25
Thermal Diffusivity, mm2/s 13
6.6
Thermal Shock Resistance, points 12 to 14
29