ASTM A216 Cast Steel vs. Z20301 Zinc

ASTM A216 cast steel belongs to the iron alloys classification, while Z20301 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A216 cast steel and the bottom bar is Z20301 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 25 to 27
53
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 72
35
Tensile Strength: Ultimate (UTS), MPa 500 to 570
160
Tensile Strength: Yield (Proof), MPa 230 to 310
130

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Maximum Temperature: Mechanical, °C 400
90
Melting Completion (Liquidus), °C 1450 to 1460
410
Melting Onset (Solidus), °C 1410
400
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 49 to 52
110
Thermal Expansion, µm/m-K 12
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1 to 7.2
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2 to 8.3
37

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
11
Density, g/cm3 7.8
6.6
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 18
53
Embodied Water, L/kg 45
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
78
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 250
96
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 18 to 20
6.7
Strength to Weight: Bending, points 18 to 20
9.9
Thermal Diffusivity, mm2/s 13 to 14
44
Thermal Shock Resistance, points 16 to 18
5.0