ASTM A217 Cast Steel vs. SAE-AISI 1524 Steel
Both ASTM A217 cast steel and SAE-AISI 1524 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is SAE-AISI 1524 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 210 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 21 to 27 | |
| 14 to 22 |
| Fatigue Strength, MPa | 200 to 320 | |
| 230 to 340 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.29 |
| Reduction in Area, % | 39 to 50 | |
| 39 to 48 |
| Shear Modulus, GPa | 73 to 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 570 to 650 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 320 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 to 600 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 to 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 to 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 26 to 50 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 to 9.2 | |
| 8.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 to 11 | |
| 9.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 to 7.0 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 20 to 28 | |
| 19 |
| Embodied Water, L/kg | 47 to 87 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 84 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 270 to 760 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 20 to 23 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 19 to 21 |
| Thermal Diffusivity, mm2/s | 6.9 to 14 | |
| 14 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 18 to 21 |