ASTM A217 Cast Steel vs. R30008 Cobalt
ASTM A217 cast steel belongs to the iron alloys classification, while R30008 cobalt belongs to the cobalt alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is R30008 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 21 to 27 | |
| 1.1 to 73 |
| Fatigue Strength, MPa | 200 to 320 | |
| 320 to 530 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 to 75 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 950 to 1700 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 500 to 1080 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 320 |
| Melting Completion (Liquidus), °C | 1450 to 1460 | |
| 1400 |
| Melting Onset (Solidus), °C | 1410 to 1420 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 to 7.0 | |
| 95 |
| Density, g/cm3 | 7.8 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
| 8.1 |
| Embodied Energy, MJ/kg | 20 to 28 | |
| 110 |
| Embodied Water, L/kg | 47 to 87 | |
| 400 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 590 to 2720 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 31 to 56 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 25 to 37 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 25 to 44 |