ASTM A228 Music Wire vs. SAE-AISI 1330 Steel

Both ASTM A228 music wire and SAE-AISI 1330 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A228 music wire and the bottom bar is SAE-AISI 1330 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 710
150 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12
11 to 23
Fatigue Strength, MPa 1280
210 to 380
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 1470
330 to 430
Tensile Strength: Ultimate (UTS), MPa 2450
520 to 710
Tensile Strength: Yield (Proof), MPa 2050
290 to 610

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 45
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 280
76 to 100
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 87
19 to 25
Strength to Weight: Bending, points 52
18 to 23
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 79
17 to 23

Alloy Composition

Carbon (C), % 0.7 to 1.0
0.28 to 0.33
Iron (Fe), % 98 to 99
97.3 to 98
Manganese (Mn), % 0.2 to 0.6
1.6 to 1.9
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.1 to 0.3
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040