ASTM A231 Spring Steel vs. AISI 317LN Stainless Steel

Both ASTM A231 spring steel and AISI 317LN stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A231 spring steel and the bottom bar is AISI 317LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 540
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
45
Fatigue Strength, MPa 1000
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 1080
430
Tensile Strength: Ultimate (UTS), MPa 1790
620
Tensile Strength: Yield (Proof), MPa 1570
270

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
1010
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
21
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.0
4.3
Embodied Energy, MJ/kg 28
59
Embodied Water, L/kg 51
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
220
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 64
22
Strength to Weight: Bending, points 42
20
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 53
14

Alloy Composition

Carbon (C), % 0.48 to 0.53
0 to 0.030
Chromium (Cr), % 0.8 to 1.1
18 to 20
Iron (Fe), % 96.7 to 97.7
57.9 to 67.9
Manganese (Mn), % 0.7 to 0.9
0 to 2.0
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
11 to 15
Nitrogen (N), % 0
0.1 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 0.75
Sulfur (S), % 0 to 0.040
0 to 0.030
Vanadium (V), % 0.15 to 0.3
0