ASTM A231 Spring Steel vs. AISI 436 Stainless Steel

Both ASTM A231 spring steel and AISI 436 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A231 spring steel and the bottom bar is AISI 436 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 540
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
25
Fatigue Strength, MPa 1000
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 1080
320
Tensile Strength: Ultimate (UTS), MPa 1790
500
Tensile Strength: Yield (Proof), MPa 1570
270

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
880
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.0
2.7
Embodied Energy, MJ/kg 28
38
Embodied Water, L/kg 51
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 64
18
Strength to Weight: Bending, points 42
18
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 53
18

Alloy Composition

Carbon (C), % 0.48 to 0.53
0 to 0.12
Chromium (Cr), % 0.8 to 1.1
16 to 18
Iron (Fe), % 96.7 to 97.7
77.8 to 83.3
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
0.75 to 1.3
Niobium (Nb), % 0
0 to 0.8
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030
Vanadium (V), % 0.15 to 0.3
0