ASTM A231 Spring Steel vs. EN 1.4600 Stainless Steel

Both ASTM A231 spring steel and EN 1.4600 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A231 spring steel and the bottom bar is EN 1.4600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14
23
Fatigue Strength, MPa 1000
290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 1080
360
Tensile Strength: Ultimate (UTS), MPa 1790
580
Tensile Strength: Yield (Proof), MPa 1570
430

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 420
730
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
27
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.0
2.0
Embodied Energy, MJ/kg 28
28
Embodied Water, L/kg 51
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
120
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 64
21
Strength to Weight: Bending, points 42
20
Thermal Diffusivity, mm2/s 14
7.3
Thermal Shock Resistance, points 53
21

Alloy Composition

Carbon (C), % 0.48 to 0.53
0 to 0.030
Chromium (Cr), % 0.8 to 1.1
11 to 13
Iron (Fe), % 96.7 to 97.7
82 to 87.7
Manganese (Mn), % 0.7 to 0.9
1.0 to 2.5
Nickel (Ni), % 0
0.3 to 1.0
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015
Titanium (Ti), % 0
0 to 0.35
Vanadium (V), % 0.15 to 0.3
0