ASTM A231 Spring Steel vs. EN 1.4749 Stainless Steel

Both ASTM A231 spring steel and EN 1.4749 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A231 spring steel and the bottom bar is EN 1.4749 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 540
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
16
Fatigue Strength, MPa 1000
190
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 1080
370
Tensile Strength: Ultimate (UTS), MPa 1790
600
Tensile Strength: Yield (Proof), MPa 1570
320

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 52
17
Thermal Expansion, µm/m-K 13
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
13
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 2.0
2.5
Embodied Energy, MJ/kg 28
36
Embodied Water, L/kg 51
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
80
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 64
22
Strength to Weight: Bending, points 42
21
Thermal Diffusivity, mm2/s 14
4.6
Thermal Shock Resistance, points 53
22

Alloy Composition

Carbon (C), % 0.48 to 0.53
0.15 to 0.2
Chromium (Cr), % 0.8 to 1.1
26 to 29
Iron (Fe), % 96.7 to 97.7
68.5 to 73.7
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015
Vanadium (V), % 0.15 to 0.3
0