ASTM A231 Spring Steel vs. S32760 Stainless Steel

Both ASTM A231 spring steel and S32760 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A231 spring steel and the bottom bar is S32760 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 540
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
28
Fatigue Strength, MPa 1000
450
Poisson's Ratio 0.29
0.27
Reduction in Area, % 46
51
Shear Modulus, GPa 73
80
Shear Strength, MPa 1080
550
Tensile Strength: Ultimate (UTS), MPa 1790
850
Tensile Strength: Yield (Proof), MPa 1570
620

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.0
4.1
Embodied Energy, MJ/kg 28
57
Embodied Water, L/kg 51
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
220
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 64
30
Strength to Weight: Bending, points 42
25
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 53
23

Alloy Composition

Carbon (C), % 0.48 to 0.53
0 to 0.030
Chromium (Cr), % 0.8 to 1.1
24 to 26
Copper (Cu), % 0
0.5 to 1.0
Iron (Fe), % 96.7 to 97.7
57.6 to 65.8
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
6.0 to 8.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.010
Tungsten (W), % 0
0.5 to 1.0
Vanadium (V), % 0.15 to 0.3