ASTM A369 Grade FP12 vs. S44626 Stainless Steel

Both ASTM A369 grade FP12 and S44626 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP12 and the bottom bar is S44626 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
23
Fatigue Strength, MPa 170
230
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 300
340
Tensile Strength: Ultimate (UTS), MPa 470
540
Tensile Strength: Yield (Proof), MPa 250
350

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
14
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.9
Embodied Energy, MJ/kg 21
42
Embodied Water, L/kg 52
160

Common Calculations

PREN (Pitting Resistance) 2.8
30
Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
110
Resilience: Unit (Modulus of Resilience), kJ/m3 160
300
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 12
4.6
Thermal Shock Resistance, points 14
18

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.060
Chromium (Cr), % 0.8 to 1.3
25 to 27
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 96.8 to 98.4
68.1 to 74.1
Manganese (Mn), % 0.3 to 0.61
0 to 0.75
Molybdenum (Mo), % 0.44 to 0.65
0.75 to 1.5
Nickel (Ni), % 0
0 to 0.5
Nitrogen (N), % 0
0 to 0.040
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0.2 to 1.0