ASTM A369 Grade FP5 vs. ACI-ASTM CA28MWV Steel

Both ASTM A369 grade FP5 and ACI-ASTM CA28MWV steel are iron alloys. They have 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is ACI-ASTM CA28MWV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
330
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
11
Fatigue Strength, MPa 160
470
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 470
1080
Tensile Strength: Yield (Proof), MPa 240
870

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 510
740
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
4.6
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
5.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
11
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
3.1
Embodied Energy, MJ/kg 23
44
Embodied Water, L/kg 69
100

Common Calculations

PREN (Pitting Resistance) 6.8
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
1920
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
38
Strength to Weight: Bending, points 17
30
Thermal Diffusivity, mm2/s 11
6.6
Thermal Shock Resistance, points 13
40

Alloy Composition

Carbon (C), % 0 to 0.15
0.2 to 0.28
Chromium (Cr), % 4.0 to 6.0
11 to 12.5
Iron (Fe), % 92.1 to 95.3
81.4 to 85.8
Manganese (Mn), % 0.3 to 0.6
0.5 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0.9 to 1.3
Nickel (Ni), % 0
0.5 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
0.9 to 1.3
Vanadium (V), % 0
0.2 to 0.3