ASTM A369 Grade FP5 vs. AISI 440B Stainless Steel

Both ASTM A369 grade FP5 and AISI 440B stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is AISI 440B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
3.0 to 18
Fatigue Strength, MPa 160
260 to 850
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 300
460 to 1110
Tensile Strength: Ultimate (UTS), MPa 470
740 to 1930
Tensile Strength: Yield (Proof), MPa 240
430 to 1860

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 510
870
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
23
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.2
Embodied Energy, MJ/kg 23
31
Embodied Water, L/kg 69
120

Common Calculations

PREN (Pitting Resistance) 6.8
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
57 to 110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
27 to 70
Strength to Weight: Bending, points 17
24 to 45
Thermal Diffusivity, mm2/s 11
6.1
Thermal Shock Resistance, points 13
27 to 70

Alloy Composition

Carbon (C), % 0 to 0.15
0.75 to 1.0
Chromium (Cr), % 4.0 to 6.0
16 to 18
Iron (Fe), % 92.1 to 95.3
78.2 to 83.3
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.75
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015