ASTM A369 Grade FP5 vs. ASTM A232 Spring Steel

Both ASTM A369 grade FP5 and ASTM A232 spring steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is ASTM A232 spring steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
540
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
14
Fatigue Strength, MPa 160
1040
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 300
1090
Tensile Strength: Ultimate (UTS), MPa 470
1790
Tensile Strength: Yield (Proof), MPa 240
1610

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
2.0
Embodied Energy, MJ/kg 23
28
Embodied Water, L/kg 69
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
64
Strength to Weight: Bending, points 17
42
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 13
53

Alloy Composition

Carbon (C), % 0 to 0.15
0.48 to 0.53
Chromium (Cr), % 4.0 to 6.0
0.8 to 1.1
Iron (Fe), % 92.1 to 95.3
96.8 to 97.7
Manganese (Mn), % 0.3 to 0.6
0.7 to 0.9
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.035
Vanadium (V), % 0
0.15 to 0.3