ASTM A369 Grade FP5 vs. AWS E316LMn

Both ASTM A369 grade FP5 and AWS E316LMn are iron alloys. They have 60% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is AWS E316LMn.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
79
Tensile Strength: Ultimate (UTS), MPa 470
620

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 13
14

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
24
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
4.6
Embodied Energy, MJ/kg 23
64
Embodied Water, L/kg 69
180

Common Calculations

PREN (Pitting Resistance) 6.8
32
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 17
20
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.040
Chromium (Cr), % 4.0 to 6.0
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 92.1 to 95.3
47.5 to 59.4
Manganese (Mn), % 0.3 to 0.6
5.0 to 8.0
Molybdenum (Mo), % 0.45 to 0.65
2.5 to 3.5
Nickel (Ni), % 0
15 to 18
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.9
Sulfur (S), % 0 to 0.025
0 to 0.030