ASTM A369 Grade FP5 vs. AWS E410

Both ASTM A369 grade FP5 and AWS E410 are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is AWS E410.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 470
580
Tensile Strength: Yield (Proof), MPa 240
440

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
28
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
7.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
2.0
Embodied Energy, MJ/kg 23
28
Embodied Water, L/kg 69
100

Common Calculations

PREN (Pitting Resistance) 6.8
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
500
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 11
7.5
Thermal Shock Resistance, points 13
16

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.12
Chromium (Cr), % 4.0 to 6.0
11 to 13.5
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 92.1 to 95.3
82.2 to 89
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.75
Nickel (Ni), % 0
0 to 0.7
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.9
Sulfur (S), % 0 to 0.025
0 to 0.030