ASTM A369 Grade FP5 vs. EN 1.0597 Cast Steel

Both ASTM A369 grade FP5 and EN 1.0597 cast steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.0597 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
18
Fatigue Strength, MPa 160
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 470
670
Tensile Strength: Yield (Proof), MPa 240
400

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 69
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
430
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 13
21

Alloy Composition

Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 4.0 to 6.0
0
Iron (Fe), % 92.1 to 95.3
99.935 to 100
Manganese (Mn), % 0.3 to 0.6
0
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.025
0 to 0.030