ASTM A369 Grade FP5 vs. EN 1.3961 Alloy

Both ASTM A369 grade FP5 and EN 1.3961 alloy are iron alloys. They have 64% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.3961 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
31
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 74
72
Shear Strength, MPa 300
300
Tensile Strength: Ultimate (UTS), MPa 470
450
Tensile Strength: Yield (Proof), MPa 240
310

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 13
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
25
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.7
4.8
Embodied Energy, MJ/kg 23
66
Embodied Water, L/kg 69
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 17
15
Strength to Weight: Bending, points 17
16
Thermal Shock Resistance, points 13
130

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.050
Chromium (Cr), % 4.0 to 6.0
0 to 0.25
Iron (Fe), % 92.1 to 95.3
60.7 to 65
Manganese (Mn), % 0.3 to 0.6
0 to 0.5
Molybdenum (Mo), % 0.45 to 0.65
0 to 1.0
Nickel (Ni), % 0
35 to 37
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.020