ASTM A369 Grade FP5 vs. EN 1.4468 Stainless Steel

Both ASTM A369 grade FP5 and EN 1.4468 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.4468 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
25
Fatigue Strength, MPa 160
380
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 470
730
Tensile Strength: Yield (Proof), MPa 240
550

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 510
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
17
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
3.8
Embodied Energy, MJ/kg 23
53
Embodied Water, L/kg 69
180

Common Calculations

PREN (Pitting Resistance) 6.8
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
170
Resilience: Unit (Modulus of Resilience), kJ/m3 140
730
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
26
Strength to Weight: Bending, points 17
23
Thermal Diffusivity, mm2/s 11
4.6
Thermal Shock Resistance, points 13
20

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 4.0 to 6.0
24.5 to 26.5
Iron (Fe), % 92.1 to 95.3
59.7 to 67.4
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.45 to 0.65
2.5 to 3.5
Nickel (Ni), % 0
5.5 to 7.0
Nitrogen (N), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.025