ASTM A369 Grade FP5 vs. EN 1.4630 Stainless Steel

Both ASTM A369 grade FP5 and EN 1.4630 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.4630 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
23
Fatigue Strength, MPa 160
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Shear Strength, MPa 300
300
Tensile Strength: Ultimate (UTS), MPa 470
480
Tensile Strength: Yield (Proof), MPa 240
250

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 510
800
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
28
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
9.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.5
Embodied Energy, MJ/kg 23
36
Embodied Water, L/kg 69
120

Common Calculations

PREN (Pitting Resistance) 6.8
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
92
Resilience: Unit (Modulus of Resilience), kJ/m3 140
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 11
7.5
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0
0 to 1.5
Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 4.0 to 6.0
13 to 16
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 92.1 to 95.3
77.1 to 86.7
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.5
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.5
Phosphorus (P), % 0 to 0.025
0 to 0.050
Silicon (Si), % 0 to 0.5
0.2 to 1.5
Sulfur (S), % 0 to 0.025
0 to 0.050
Titanium (Ti), % 0
0.15 to 0.8