ASTM A369 Grade FP5 vs. EN 1.4669 Stainless Steel

Both ASTM A369 grade FP5 and EN 1.4669 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.4669 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
28
Fatigue Strength, MPa 160
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
78
Shear Strength, MPa 300
500
Tensile Strength: Ultimate (UTS), MPa 470
780
Tensile Strength: Yield (Proof), MPa 240
450

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 510
1030
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
13
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.6
Embodied Energy, MJ/kg 23
38
Embodied Water, L/kg 69
160

Common Calculations

PREN (Pitting Resistance) 6.8
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
190
Resilience: Unit (Modulus of Resilience), kJ/m3 140
510
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
28
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 13
21

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.045
Chromium (Cr), % 4.0 to 6.0
21.5 to 24
Copper (Cu), % 0
1.6 to 3.0
Iron (Fe), % 92.1 to 95.3
65.2 to 74.8
Manganese (Mn), % 0.3 to 0.6
1.0 to 3.0
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.5
Nickel (Ni), % 0
1.0 to 3.0
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030