MakeItFrom.com
Menu (ESC)

ASTM A369 Grade FP5 vs. EN 1.4877 Stainless Steel

Both ASTM A369 grade FP5 and EN 1.4877 stainless steel are iron alloys. They have 45% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.4877 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
36
Fatigue Strength, MPa 160
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
79
Shear Strength, MPa 300
420
Tensile Strength: Ultimate (UTS), MPa 470
630
Tensile Strength: Yield (Proof), MPa 240
200

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Maximum Temperature: Mechanical, °C 510
1150
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
37
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.7
6.2
Embodied Energy, MJ/kg 23
89
Embodied Water, L/kg 69
220

Common Calculations

PREN (Pitting Resistance) 6.8
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
180
Resilience: Unit (Modulus of Resilience), kJ/m3 140
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 11
3.2
Thermal Shock Resistance, points 13
15

Alloy Composition

Aluminum (Al), % 0
0 to 0.025
Carbon (C), % 0 to 0.15
0.040 to 0.080
Cerium (Ce), % 0
0.050 to 0.1
Chromium (Cr), % 4.0 to 6.0
26 to 28
Iron (Fe), % 92.1 to 95.3
36.4 to 42.3
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0
Nickel (Ni), % 0
31 to 33
Niobium (Nb), % 0
0.6 to 1.0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.010