ASTM A369 Grade FP5 vs. EN 1.5520 Steel

Both ASTM A369 grade FP5 and EN 1.5520 steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.5520 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
120 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
11 to 21
Fatigue Strength, MPa 160
210 to 300
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 300
290 to 340
Tensile Strength: Ultimate (UTS), MPa 470
410 to 1410
Tensile Strength: Yield (Proof), MPa 240
300 to 480

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
50
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 69
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
42 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240 to 600
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
15 to 50
Strength to Weight: Bending, points 17
16 to 36
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 13
12 to 41

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.15
0.15 to 0.2
Chromium (Cr), % 4.0 to 6.0
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 92.1 to 95.3
97.7 to 98.9
Manganese (Mn), % 0.3 to 0.6
0.9 to 1.2
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.025