ASTM A369 Grade FP5 vs. EN 1.7336 Steel

Both ASTM A369 grade FP5 and EN 1.7336 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.7336 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
22
Fatigue Strength, MPa 160
240 to 310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 300
370
Tensile Strength: Ultimate (UTS), MPa 470
590
Tensile Strength: Yield (Proof), MPa 240
340 to 440

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Maximum Temperature: Mechanical, °C 510
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
3.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.6
Embodied Energy, MJ/kg 23
21
Embodied Water, L/kg 69
53

Common Calculations

PREN (Pitting Resistance) 6.8
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
310 to 510
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.17
Chromium (Cr), % 4.0 to 6.0
1.0 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 92.1 to 95.3
95.6 to 97.7
Manganese (Mn), % 0.3 to 0.6
0.4 to 0.65
Molybdenum (Mo), % 0.45 to 0.65
0.45 to 0.65
Nickel (Ni), % 0
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.025
0 to 0.015
Silicon (Si), % 0 to 0.5
0.5 to 0.8
Sulfur (S), % 0 to 0.025
0 to 0.0050