ASTM A369 Grade FP5 vs. EN 1.8967 Steel

Both ASTM A369 grade FP5 and EN 1.8967 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is EN 1.8967 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
16
Fatigue Strength, MPa 160
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 300
350
Tensile Strength: Ultimate (UTS), MPa 470
570
Tensile Strength: Yield (Proof), MPa 240
340

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
3.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.8
Embodied Energy, MJ/kg 23
25
Embodied Water, L/kg 69
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
78
Resilience: Unit (Modulus of Resilience), kJ/m3 140
300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 11
10
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0 to 0.15
0 to 0.19
Chromium (Cr), % 4.0 to 6.0
0.35 to 0.85
Copper (Cu), % 0
0.2 to 0.6
Iron (Fe), % 92.1 to 95.3
94.6 to 99
Manganese (Mn), % 0.3 to 0.6
0.45 to 1.6
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.35
Nickel (Ni), % 0
0 to 0.7
Niobium (Nb), % 0
0 to 0.065
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.035
Titanium (Ti), % 0
0 to 0.12
Vanadium (V), % 0
0 to 0.14
Zirconium (Zr), % 0
0 to 0.17