ASTM A369 Grade FP5 vs. SAE-AISI 50B60 Steel

Both ASTM A369 grade FP5 and SAE-AISI 50B60 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is SAE-AISI 50B60 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
12 to 20
Fatigue Strength, MPa 160
240 to 330
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Shear Strength, MPa 300
380
Tensile Strength: Ultimate (UTS), MPa 470
610 to 630
Tensile Strength: Yield (Proof), MPa 240
350 to 530

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
410
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
45
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 69
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
71 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
330 to 750
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
22 to 23
Strength to Weight: Bending, points 17
20 to 21
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 13
20

Alloy Composition

Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0 to 0.15
0.56 to 0.64
Chromium (Cr), % 4.0 to 6.0
0.4 to 0.6
Iron (Fe), % 92.1 to 95.3
97.3 to 98.1
Manganese (Mn), % 0.3 to 0.6
0.75 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.040