ASTM A369 Grade FP5 vs. SAE-AISI M43 Steel

Both ASTM A369 grade FP5 and SAE-AISI M43 steel are iron alloys. They have 79% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is SAE-AISI M43 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
77
Tensile Strength: Ultimate (UTS), MPa 470
810 to 2290

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1460
1550
Melting Onset (Solidus), °C 1420
1500
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 40
19
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
33
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.7
8.5
Embodied Energy, MJ/kg 23
120
Embodied Water, L/kg 69
140

Common Calculations

PREN (Pitting Resistance) 6.8
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
27 to 77
Strength to Weight: Bending, points 17
24 to 47
Thermal Diffusivity, mm2/s 11
5.3
Thermal Shock Resistance, points 13
25 to 71

Alloy Composition

Carbon (C), % 0 to 0.15
1.2 to 1.3
Chromium (Cr), % 4.0 to 6.0
3.5 to 4.3
Cobalt (Co), % 0
7.8 to 8.8
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 92.1 to 95.3
70.8 to 76
Manganese (Mn), % 0.3 to 0.6
0.2 to 0.4
Molybdenum (Mo), % 0.45 to 0.65
7.5 to 8.5
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.5
0.15 to 0.65
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
2.3 to 3.0
Vanadium (V), % 0
1.5 to 1.8