ASTM A369 Grade FP5 vs. S35115 Stainless Steel

Both ASTM A369 grade FP5 and S35115 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 58% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP5 and the bottom bar is S35115 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
46
Fatigue Strength, MPa 160
280
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
79
Shear Strength, MPa 300
470
Tensile Strength: Ultimate (UTS), MPa 470
670
Tensile Strength: Yield (Proof), MPa 240
310

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Maximum Temperature: Mechanical, °C 510
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
26
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
4.8
Embodied Energy, MJ/kg 23
67
Embodied Water, L/kg 69
190

Common Calculations

PREN (Pitting Resistance) 6.8
35
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
250
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 11
3.9
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 4.0 to 6.0
23 to 25
Iron (Fe), % 92.1 to 95.3
47.6 to 55.8
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
1.5 to 2.5
Nickel (Ni), % 0
19 to 22
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.5
0.5 to 1.5
Sulfur (S), % 0 to 0.025
0 to 0.015