ASTM A369 Grade FP9 vs. ZA-27

ASTM A369 grade FP9 belongs to the iron alloys classification, while ZA-27 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP9 and the bottom bar is ZA-27.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
100 to 120
Elastic (Young's, Tensile) Modulus, GPa 190
78
Elongation at Break, % 20
2.0 to 4.5
Fatigue Strength, MPa 160
110 to 170
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 75
31
Shear Strength, MPa 300
230 to 330
Tensile Strength: Ultimate (UTS), MPa 470
400 to 430
Tensile Strength: Yield (Proof), MPa 240
260 to 370

Thermal Properties

Latent Heat of Fusion, J/g 270
130
Maximum Temperature: Mechanical, °C 600
120
Melting Completion (Liquidus), °C 1450
480
Melting Onset (Solidus), °C 1410
380
Specific Heat Capacity, J/kg-K 480
530
Thermal Conductivity, W/m-K 26
130
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.0
30
Electrical Conductivity: Equal Weight (Specific), % IACS 10
53

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
11
Density, g/cm3 7.8
5.0
Embodied Carbon, kg CO2/kg material 2.0
4.2
Embodied Energy, MJ/kg 28
80
Embodied Water, L/kg 87
570

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
8.1 to 18
Resilience: Unit (Modulus of Resilience), kJ/m3 140
420 to 890
Stiffness to Weight: Axial, points 14
8.6
Stiffness to Weight: Bending, points 25
28
Strength to Weight: Axial, points 17
22 to 24
Strength to Weight: Bending, points 17
24 to 25
Thermal Diffusivity, mm2/s 6.9
47
Thermal Shock Resistance, points 13
14 to 15

Alloy Composition

Aluminum (Al), % 0
25 to 28
Cadmium (Cd), % 0
0 to 0.0060
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 8.0 to 10
0
Copper (Cu), % 0
2.0 to 2.5
Iron (Fe), % 87.1 to 90.3
0 to 0.1
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 0
0.010 to 0.020
Manganese (Mn), % 0.3 to 0.6
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.5 to 1.0
0 to 0.080
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
69.3 to 73