ASTM A369 Grade FP92 vs. AISI 204 Stainless Steel

Both ASTM A369 grade FP92 and AISI 204 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP92 and the bottom bar is AISI 204 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
210 to 330
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
23 to 39
Fatigue Strength, MPa 330
320 to 720
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 440
500 to 700
Tensile Strength: Ultimate (UTS), MPa 710
730 to 1100
Tensile Strength: Yield (Proof), MPa 490
380 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 590
850
Melting Completion (Liquidus), °C 1490
1410
Melting Onset (Solidus), °C 1450
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 26
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 10
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 11
10
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 2.8
2.4
Embodied Energy, MJ/kg 40
35
Embodied Water, L/kg 89
130

Common Calculations

PREN (Pitting Resistance) 14
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
240 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 620
360 to 2940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
27 to 40
Strength to Weight: Bending, points 22
24 to 31
Thermal Diffusivity, mm2/s 6.9
4.1
Thermal Shock Resistance, points 19
16 to 24

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.070 to 0.13
0 to 0.030
Chromium (Cr), % 8.5 to 9.5
15 to 17
Iron (Fe), % 85.8 to 89.1
69.6 to 76.4
Manganese (Mn), % 0.3 to 0.6
7.0 to 9.0
Molybdenum (Mo), % 0.3 to 0.6
0
Nickel (Ni), % 0 to 0.4
1.5 to 3.0
Niobium (Nb), % 0.040 to 0.090
0
Nitrogen (N), % 0.030 to 0.070
0.15 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 1.5 to 2.0
0
Vanadium (V), % 0.15 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0