ASTM A369 Grade FP92 vs. EN 1.5515 Steel

Both ASTM A369 grade FP92 and EN 1.5515 steel are iron alloys. They have 88% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP92 and the bottom bar is EN 1.5515 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
150 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 710
490 to 1760

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 590
400
Melting Completion (Liquidus), °C 1490
1460
Melting Onset (Solidus), °C 1450
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
48
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.3
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 11
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.4
Embodied Energy, MJ/kg 40
19
Embodied Water, L/kg 89
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
17 to 63
Strength to Weight: Bending, points 22
18 to 41
Thermal Diffusivity, mm2/s 6.9
13
Thermal Shock Resistance, points 19
14 to 52

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0010 to 0.0060
0.00080 to 0.0050
Carbon (C), % 0.070 to 0.13
0.35 to 0.4
Chromium (Cr), % 8.5 to 9.5
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 85.8 to 89.1
97.8 to 98.9
Manganese (Mn), % 0.3 to 0.6
0.6 to 0.9
Molybdenum (Mo), % 0.3 to 0.6
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.040 to 0.090
0
Nitrogen (N), % 0.030 to 0.070
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.5
0.15 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 1.5 to 2.0
0
Vanadium (V), % 0.15 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0