ASTM A369 Grade FPB vs. ASTM A210 Steel

Both ASTM A369 grade FPB and ASTM A210 steel are iron alloys.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is ASTM A210 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
140 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
34
Fatigue Strength, MPa 180
230 to 250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 290
320 to 360
Tensile Strength: Ultimate (UTS), MPa 470
470 to 540
Tensile Strength: Yield (Proof), MPa 270
290 to 310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460 to 1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
52 to 53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.0 to 8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
45 to 46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 190
230 to 250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
17 to 19
Strength to Weight: Bending, points 17
17 to 19
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 15
15 to 17