ASTM A369 Grade FPB vs. AWS ENiCrFe-2

ASTM A369 grade FPB belongs to the iron alloys classification, while AWS ENiCrFe-2 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is AWS ENiCrFe-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
28
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
74
Tensile Strength: Ultimate (UTS), MPa 470
790

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
65
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.4
11
Embodied Energy, MJ/kg 18
160
Embodied Water, L/kg 46
260

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 17
26
Strength to Weight: Bending, points 17
22
Thermal Shock Resistance, points 15
24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.3
0 to 0.1
Chromium (Cr), % 0
13 to 17
Cobalt (Co), % 0
0 to 0.12
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 98.1 to 99.61
0 to 12
Manganese (Mn), % 0.29 to 1.1
1.0 to 3.5
Molybdenum (Mo), % 0
0.5 to 2.5
Nickel (Ni), % 0
62 to 85
Niobium (Nb), % 0
0.5 to 4.0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.1 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.020
Residuals, % 0
0 to 0.5