ASTM A369 Grade FPB vs. EN 1.0143 Steel

Both ASTM A369 grade FPB and EN 1.0143 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is EN 1.0143 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
21
Fatigue Strength, MPa 180
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 290
300
Tensile Strength: Ultimate (UTS), MPa 470
470
Tensile Strength: Yield (Proof), MPa 270
250

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
85
Resilience: Unit (Modulus of Resilience), kJ/m3 190
170
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 17
17
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.21
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 98.1 to 99.61
97.5 to 100
Manganese (Mn), % 0.29 to 1.1
0 to 1.6
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.1 to 0.5
0
Sulfur (S), % 0 to 0.035
0 to 0.040