ASTM A369 Grade FPB vs. EN 2.4633 Nickel

ASTM A369 grade FPB belongs to the iron alloys classification, while EN 2.4633 nickel belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is EN 2.4633 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
34
Fatigue Strength, MPa 180
230
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 290
510
Tensile Strength: Ultimate (UTS), MPa 470
760
Tensile Strength: Yield (Proof), MPa 270
310

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1350
Melting Onset (Solidus), °C 1420
1300
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
11
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
50
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.4
8.4
Embodied Energy, MJ/kg 18
120
Embodied Water, L/kg 46
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
210
Resilience: Unit (Modulus of Resilience), kJ/m3 190
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
26
Strength to Weight: Bending, points 17
23
Thermal Diffusivity, mm2/s 14
2.9
Thermal Shock Resistance, points 15
22

Alloy Composition

Aluminum (Al), % 0
1.8 to 2.4
Carbon (C), % 0 to 0.3
0.15 to 0.25
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 98.1 to 99.61
8.0 to 11
Manganese (Mn), % 0.29 to 1.1
0 to 0.5
Nickel (Ni), % 0
58.8 to 65.9
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0.1 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.010
Titanium (Ti), % 0
0.1 to 0.2
Yttrium (Y), % 0
0.050 to 0.12
Zirconium (Zr), % 0
0.010 to 0.1