ASTM A369 Grade FPB vs. Grade CW6MC Nickel

ASTM A369 grade FPB belongs to the iron alloys classification, while grade CW6MC nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is grade CW6MC nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
28
Fatigue Strength, MPa 180
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 470
540
Tensile Strength: Yield (Proof), MPa 270
310

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 52
11
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
80
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.4
14
Embodied Energy, MJ/kg 18
200
Embodied Water, L/kg 46
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
130
Resilience: Unit (Modulus of Resilience), kJ/m3 190
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 17
17
Thermal Diffusivity, mm2/s 14
2.8
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.060
Chromium (Cr), % 0
20 to 23
Iron (Fe), % 98.1 to 99.61
0 to 5.0
Manganese (Mn), % 0.29 to 1.1
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
55.4 to 68.9
Niobium (Nb), % 0
3.2 to 4.5
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0.1 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.030