ASTM A369 Grade FPB vs. Nickel 625

ASTM A369 grade FPB belongs to the iron alloys classification, while nickel 625 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is nickel 625.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
33 to 34
Fatigue Strength, MPa 180
240 to 320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
79
Shear Strength, MPa 290
530 to 600
Tensile Strength: Ultimate (UTS), MPa 470
790 to 910
Tensile Strength: Yield (Proof), MPa 270
320 to 450

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1350
Melting Onset (Solidus), °C 1420
1290
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 52
11
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
80
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.4
14
Embodied Energy, MJ/kg 18
190
Embodied Water, L/kg 46
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
220 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 190
260 to 490
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 17
26 to 29
Strength to Weight: Bending, points 17
22 to 24
Thermal Diffusivity, mm2/s 14
2.9
Thermal Shock Resistance, points 15
22 to 25

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0 to 0.3
0 to 0.1
Chromium (Cr), % 0
20 to 23
Cobalt (Co), % 0
0 to 1.0
Iron (Fe), % 98.1 to 99.61
0 to 5.0
Manganese (Mn), % 0.29 to 1.1
0 to 0.5
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
58 to 68.9
Niobium (Nb), % 0
3.2 to 4.2
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0.1 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.015
Titanium (Ti), % 0
0 to 0.4