ASTM A369 Grade FPB vs. N08024 Nickel

ASTM A369 grade FPB belongs to the iron alloys classification, while N08024 nickel belongs to the nickel alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is N08024 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
34
Fatigue Strength, MPa 180
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 290
410
Tensile Strength: Ultimate (UTS), MPa 470
620
Tensile Strength: Yield (Proof), MPa 270
270

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
990
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 52
12
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
41
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.4
7.2
Embodied Energy, MJ/kg 18
99
Embodied Water, L/kg 46
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
170
Resilience: Unit (Modulus of Resilience), kJ/m3 190
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 14
3.2
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.030
Chromium (Cr), % 0
22.5 to 25
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 98.1 to 99.61
26.6 to 38.4
Manganese (Mn), % 0.29 to 1.1
0 to 1.0
Molybdenum (Mo), % 0
3.5 to 5.0
Nickel (Ni), % 0
35 to 40
Niobium (Nb), % 0
0.15 to 0.35
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.1 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.035