ASTM A369 Grade FPB vs. S40920 Stainless Steel

Both ASTM A369 grade FPB and S40920 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FPB and the bottom bar is S40920 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
22
Fatigue Strength, MPa 180
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 290
270
Tensile Strength: Ultimate (UTS), MPa 470
430
Tensile Strength: Yield (Proof), MPa 270
190

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
710
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
26
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
6.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 18
28
Embodied Water, L/kg 46
94

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
78
Resilience: Unit (Modulus of Resilience), kJ/m3 190
97
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
15
Strength to Weight: Bending, points 17
16
Thermal Diffusivity, mm2/s 14
6.9
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.030
Chromium (Cr), % 0
10.5 to 11.7
Iron (Fe), % 98.1 to 99.61
85.1 to 89.4
Manganese (Mn), % 0.29 to 1.1
0 to 1.0
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.1
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.1 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.020
Titanium (Ti), % 0
0.15 to 0.5