ASTM A372 Grade H Steel vs. AISI 440C Stainless Steel

Both ASTM A372 grade H steel and AISI 440C stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade H steel and the bottom bar is AISI 440C stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20 to 22
2.0 to 14
Fatigue Strength, MPa 310 to 380
260 to 840
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 410 to 570
430 to 1120
Tensile Strength: Ultimate (UTS), MPa 650 to 910
710 to 1970
Tensile Strength: Yield (Proof), MPa 430 to 550
450 to 1900

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 410
870
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
22
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
2.2
Embodied Energy, MJ/kg 20
31
Embodied Water, L/kg 49
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 160
39 to 88
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 32
26 to 71
Strength to Weight: Bending, points 21 to 27
23 to 46
Thermal Diffusivity, mm2/s 12
6.0
Thermal Shock Resistance, points 19 to 27
26 to 71

Alloy Composition

Carbon (C), % 0.3 to 0.4
1.0 to 1.2
Chromium (Cr), % 0.4 to 0.65
16 to 18
Iron (Fe), % 97.3 to 98.3
78 to 83.1
Manganese (Mn), % 0.75 to 1.1
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
0 to 0.75
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015