ASTM A372 Grade H Steel vs. EN 1.6771 Steel

Both ASTM A372 grade H steel and EN 1.6771 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade H steel and the bottom bar is EN 1.6771 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 280
280 to 350
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20 to 22
8.0 to 8.7
Fatigue Strength, MPa 310 to 380
440 to 680
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 650 to 910
930 to 1180
Tensile Strength: Yield (Proof), MPa 430 to 550
740 to 1140

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.9
Embodied Energy, MJ/kg 20
25
Embodied Water, L/kg 49
58

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 160
75 to 93
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 810
1460 to 3450
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 32
33 to 41
Strength to Weight: Bending, points 21 to 27
27 to 31
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 19 to 27
27 to 35

Alloy Composition

Carbon (C), % 0.3 to 0.4
0.27 to 0.33
Chromium (Cr), % 0.4 to 0.65
0.8 to 1.2
Iron (Fe), % 97.3 to 98.3
92.2 to 95
Manganese (Mn), % 0.75 to 1.1
0.6 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
0.3 to 0.6
Nickel (Ni), % 0
3.0 to 4.0
Phosphorus (P), % 0 to 0.015
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.020

Comparable Variants