ASTM A372 Grade J Steel vs. AISI 442 Stainless Steel

Both ASTM A372 grade J steel and AISI 442 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is AISI 442 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 22
23
Fatigue Strength, MPa 310 to 570
210
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
78
Shear Strength, MPa 410 to 630
370
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
580
Tensile Strength: Yield (Proof), MPa 430 to 850
310

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
960
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
22
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
10
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
2.3
Embodied Energy, MJ/kg 20
32
Embodied Water, L/kg 51
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
110
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
250
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 36
21
Strength to Weight: Bending, points 21 to 29
20
Thermal Diffusivity, mm2/s 12
5.8
Thermal Shock Resistance, points 19 to 30
20

Alloy Composition

Carbon (C), % 0.35 to 0.5
0 to 0.2
Chromium (Cr), % 0.8 to 1.2
18 to 23
Iron (Fe), % 96.7 to 97.8
74.1 to 82
Manganese (Mn), % 0.75 to 1.1
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
0
Nickel (Ni), % 0
0 to 0.6
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.040