ASTM A372 Grade J Steel vs. EN 1.7230 Steel

Both ASTM A372 grade J steel and EN 1.7230 steel are iron alloys. Their average alloy composition is basically identical. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is EN 1.7230 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
220 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 22
11 to 12
Fatigue Strength, MPa 310 to 570
320 to 460
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
720 to 910
Tensile Strength: Yield (Proof), MPa 430 to 850
510 to 740

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 20
20
Embodied Water, L/kg 51
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
79 to 97
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
700 to 1460
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 36
26 to 32
Strength to Weight: Bending, points 21 to 29
23 to 27
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 19 to 30
21 to 27

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.3 to 0.37
Chromium (Cr), % 0.8 to 1.2
0.8 to 1.2
Iron (Fe), % 96.7 to 97.8
96.7 to 98.3
Manganese (Mn), % 0.75 to 1.1
0.5 to 0.8
Molybdenum (Mo), % 0.15 to 0.25
0.15 to 0.3
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.030

Comparable Variants