ASTM A372 Grade J Steel vs. EN 1.7362 Steel

Both ASTM A372 grade J steel and EN 1.7362 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is EN 1.7362 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 22
21 to 22
Fatigue Strength, MPa 310 to 570
140 to 250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 410 to 630
320 to 370
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
510 to 600
Tensile Strength: Yield (Proof), MPa 430 to 850
200 to 360

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 420
510
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
4.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 20
23
Embodied Water, L/kg 51
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
100 to 340
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 36
18 to 21
Strength to Weight: Bending, points 21 to 29
18 to 20
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 19 to 30
14 to 17

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.1 to 0.15
Chromium (Cr), % 0.8 to 1.2
4.0 to 6.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.7 to 97.8
91.5 to 95.2
Manganese (Mn), % 0.75 to 1.1
0.3 to 0.6
Molybdenum (Mo), % 0.15 to 0.25
0.45 to 0.65
Nickel (Ni), % 0
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0.15 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.0050