ASTM A372 Grade J Steel vs. EN 1.7380 Steel

Both ASTM A372 grade J steel and EN 1.7380 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is EN 1.7380 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
160 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 22
19 to 20
Fatigue Strength, MPa 310 to 570
200 to 230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 410 to 630
330 to 350
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
540 to 550
Tensile Strength: Yield (Proof), MPa 430 to 850
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 420
460
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
3.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 20
23
Embodied Water, L/kg 51
59

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
87 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
230 to 280
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 36
19 to 20
Strength to Weight: Bending, points 21 to 29
19
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 19 to 30
15 to 16

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.080 to 0.14
Chromium (Cr), % 0.8 to 1.2
2.0 to 2.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.7 to 97.8
94.6 to 96.6
Manganese (Mn), % 0.75 to 1.1
0.4 to 0.8
Molybdenum (Mo), % 0.15 to 0.25
0.9 to 1.1
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0.15 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.010

Comparable Variants